Secondary high alumina bricks are refractory materials made of high alumina bauxite as the main raw material, with the main component being alumina (Al₂O₃) with a content of not less than 65%.
They are made by using different grades of bauxite clinker and formula binder, and then formed and fired at high temperature.
Secondary high alumina bricks have good refractory properties and corrosion resistance, and are suitable for environments such as high-temperature furnaces.
(1) High refractoriness
(2) High refractoriness under load
(3) Strong slag resistance
(4) High compressive strength
(5) Good stability
(6) Good wear resistance
(1) Iron and steel manufacturing industry: blast furnace, hot blast furnace, electric furnace, ladle, tundish, heating furnace, refining furnace, heating furnace, annealing furnace, cupola
(2) Nonferrous metal industry: smelting furnace, refining furnace, reverberatory furnace, converter furnace.
(3) Building materials industry: cement kiln, glass kiln, ceramic kiln, lime kiln, kiln car, tunnel kiln
(4) Energy and incineration: coke oven, circulating fluidized bed boiler, carbon roaster, incinerator.
|
Item |
Index |
||||
|
Model |
SK35 |
SK36 |
SK37 |
SK38 |
SK39 |
|
Al2O3/% |
≥48 |
≥55 |
≥65 |
≥75 |
≥80 |
|
Fe2O3/% |
≤2 |
≤2 |
≤2 |
≤2 |
≤2 |
|
Body density（g/cm3） |
2.15 |
2.2 |
2.3 |
2.4 |
2.5 |
|
Refractory |
≥1750 °C |
≥1770 °C |
≥1790 °C |
≥1790 °C |
≥1790 °C |
|
Change in heating permanent line/% |
1450℃×2h -0.4~0.1 |
1450℃×2h -0.4~0.1 |
1450℃×2h -0.4~0.1 |
1500℃×2h -0.4~0.2 |
1500℃×2h -0.4~0.2 |
|
Cold pressing strength |
≥39Mpa |
≥44Mpa |
≥49Mpa |
≥54Mpa |
≥65Mpa |
|
Apparent porosity (≤) |
≤22% |
≤22% |
≤23% |
≤23% |
≤21% |
|
Load softening temperature [0.2MPa*0.6%]≥ |
≥1420 °C |
≥1470 °C |
≥1500 °C |
≥1520 °C |
≥1530 °C |
High alumina poly light brick is a high quality lightweight refractory material.
Alumina content is 48%-60% Refractoriness is above 1770℃