First-grade high alumina brick-chip is a high-quality refractory material, the main component of which is alumina (Al₂O₃) with a content of not less than 75%.
It is made by using different grades of bauxite clinker and formula binder, and undergoing high-temperature mixing, forming, drying, sintering, brick press molding and high-temperature calcination.
First-grade high alumina brick has extremely high refractory performance and resistance to chemical erosion, and is mainly used in high-temperature industrial equipment.
(1) High refractoriness
(2) High refractoriness under load
(3) Strong slag resistance
(4) High compressive strength
(5) Good stability
(6) Good wear resistance
(1) Iron and steel manufacturing industry: blast furnace, hot blast furnace, electric furnace, ladle, tundish, heating furnace, refining furnace, heating furnace, annealing furnace, cupola
(2) Nonferrous metal industry: smelting furnace, refining furnace, reverberatory furnace, converter furnace.
(3) Building materials industry: cement kiln, glass kiln, ceramic kiln, lime kiln, kiln car, tunnel kiln
(4) Energy and incineration: coke oven, circulating fluidized bed boiler, carbon roaster, incinerator.
|
Item |
Index |
||||
|
Model |
SK35 |
SK36 |
SK37 |
SK38 |
SK39 |
|
Al2O3/% |
≥48 |
≥55 |
≥65 |
≥75 |
≥80 |
|
Fe2O3/% |
≤2 |
≤2 |
≤2 |
≤2 |
≤2 |
|
Body density（g/cm3） |
2.15 |
2.2 |
2.3 |
2.4 |
2.5 |
|
Refractory |
≥1750 °C |
≥1770 °C |
≥1790 °C |
≥1790 °C |
≥1790 °C |
|
Change in heating permanent line/% |
1450℃×2h -0.4~0.1 |
1450℃×2h -0.4~0.1 |
1450℃×2h -0.4~0.1 |
1500℃×2h -0.4~0.2 |
1500℃×2h -0.4~0.2 |
|
Cold pressing strength |
≥39Mpa |
≥44Mpa |
≥49Mpa |
≥54Mpa |
≥65Mpa |
|
Apparent porosity (≤) |
≤22% |
≤22% |
≤23% |
≤23% |
≤21% |
|
Load softening temperature [0.2MPa*0.6%]≥ |
≥1420 °C |
≥1470 °C |
≥1500 °C |
≥1520 °C |
≥1530 °C |
High alumina poly light brick is a high quality lightweight refractory material.
Checker bricks are heat transfer media used in the regenerative chambers of blast furnaces and hot blast stoves.
Mullite lightweight insulation brick is a high-quality insulation material.
Low creep clay bricks have a low creep rate in high temperature environments and can maintain good shape and dimensional stability for a long time.
Silica-molybdenum bricks have high resistance to chemical erosion and excellent wear resistance, and are the preferred material for the transition zone and preheating zone of large cement kilns.
Made from industrial alumina and refractory kaolin as the main raw materials, produced through scientific formulation...